Self-assembled arrays of ZnO nanoparticles and their application as varistor materialsElectronic supplementary information (ESI) available: XRD plots and FESEM images. See http://www.rsc.org/suppdata/jm/b4/b400927d/

Pillai, Suresh C. and Kelly, John M. and McCormack, Declan E. and Ramesh, Raghavendra (2004) Self-assembled arrays of ZnO nanoparticles and their application as varistor materialsElectronic supplementary information (ESI) available: XRD plots and FESEM images. See http://www.rsc.org/suppdata/jm/b4/b400927d/. Journal of Materials Chemistry, 14 (10). p. 1572. ISSN 0959-9428

[img]
Preview
PDF
Self-assembled arrays of ZnO nanoparticles and their application.pdf

Download (893kB) | Preview
Official URL: http://dx.doi.org/10.1039/b400927d

Abstract

Linear arrays of ZnO nanoparticles have been successfully prepared by a simple sol–gel condensation reaction involving chemical modifiers, followed by drying (80 uC) and calcination (500 uC). The calcined material (nanoarray ZnO) is composed of approximately spherical nanoparticles of average diameter 21 ¡ 3 nm, selfassembled to form arrays extending in length to 2–4 mm. The morphology of the ZnO is found to depend sensitively on the amounts of chemical modifiers present. In their absence the ZnO produced (nano-ZnO) is an unstructured agglomerate of nanoparticles. The mechanism for formation of these linear arrays has been investigated by examining the intermediates formed at 80 uC and 250 uC using XRD and TEM and by following the decomposition reactions using TGA and DSC. Varistors prepared from the nano-array ZnO by sintering (1050 uC) with appropriate mixtures of metal oxides showed a breakdown voltage of 786 ¡ 30 V mm21, which is substantially higher than that of samples prepared under similar conditions from either micronsized commercial ZnO (507 ¡ 30 V mm21) or from nano-ZnO (683 ¡ 30 V mm21).

Item Type: Article
Departments or Groups: South East Applied Materials Research Centre
Divisions: School of Engineering
Depositing User: Ramesh Raghavendra
Date Deposited: 12 Mar 2014 10:17
Last Modified: 22 Aug 2016 10:27
URI: http://repository.wit.ie/id/eprint/2784

Actions (login required)

View Item View Item